钟泽辉,卞喻,徐军,孔繁辉.以改性丙烯酸酯乳液为连结料的水性油墨制备[J].包装工程,2013,34(21):95-99.
ZHONG Ze-hui,BIAN Yu,XU Jun,KONG Fan-hui.Preparation of Water-based Ink Based on Modified Acrylate Emulsion[J].Packaging Engineering,2013,34(21):95-99. |
| 以改性丙烯酸酯乳液为连结料的水性油墨制备 |
| Preparation of Water-based Ink Based on Modified Acrylate Emulsion |
| 投稿时间：2012-11-25 修订日期：2013-11-10 |
| DOI： |
| 中文关键词: 水性丙烯酸酯乳液 水性油墨 交联改性 双丙酮丙烯酰胺 |
| 英文关键词: waterborne acrylic emulsion water-based ink crosslinking modification diacetone acrylamide |
| 基金项目:湖南省自然科学基金资助项目(12JJ9012) |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 采用半连续乳化法制备了双丙酮丙烯酰胺-己二酸二酰肼改性的丙烯酸酯乳液,配以蓝色碱性颜料配制成水性油墨,讨论了交联体系改性对水性油墨各性能的影响。结果表明,随着DAAM-ADH 的质量分数由0 增加到3%,丙烯酸酯乳液固含量增加,粒径变小,水性油墨的黏度增大,稳定性得到了改善,附着牢度增大,耐水性耐酸碱性增强;当DAAM-ADH 的质量分数继续增加至5%时,水性油墨的黏度显著增大,导致物理凝胶。 |
| 英文摘要: |
| Water-based ink was prepared by mixing diacetone acrylamide-adipate hydrazide modified acrylate emulsion, which was synthesized by semi-continuous emulsion polymerization with blue alkaline pigment. The effect of crosslinking system modification on performances of the water-based ink was studied. The results showed that when the content of DAAM-ADH increase to 3% from 0%, the solid content of acrylate emulsion increases, the particle size decreases, the viscosity of water-based ink increases, the stability improved, the adhesion increases, the water resistance and acid-alkali resistance became stronger. When the content of DAAM-ADH is up to 5%, the viscosity of water-based ink increase significantly, this results in physical gel. |
|