王鑫婷,曹国荣,李东立,杨美琪.PVA胶带的制备及力学性能研究[J].包装工程,2018,39(5):13-15.
WANG Xin-ting,CAO Guo-rong,LI Dong-li,YANG Mei-qi.Preparation and Mechanical Property of PVA Tape[J].Packaging Engineering,2018,39(5):13-15. |
| PVA胶带的制备及力学性能研究 |
| Preparation and Mechanical Property of PVA Tape |
| 投稿时间：2017-11-23 修订日期：2018-03-10 |
| DOI：10.19554/j.cnki.1001-3563.2018.05.003 |
| 中文关键词: PVA 粘合剂 胶带 制备 力学性能 |
| 英文关键词: PVA adhesive tape preparation mechanical property |
| 基金项目:包装工程专业教学团队（建设）（22150116006/017）；京津冀高校协同培养印刷与包装专业创新创业人才的研究（22150116007/055） |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 用水溶PVA薄膜代替不可降解BOPP薄膜作为胶带基材。方法 试验分别测试PVA和BOPP薄膜（未涂布）的拉伸强度和断裂伸长率，涂布水性压敏胶的PVA和BOPP薄膜以及涂布热熔胶的PVA薄膜的拉伸强度、断裂伸长率、初粘性和180°剥离强度。结果 BOPP薄膜的拉伸强度为34.32 N/cm，略高于PVA薄膜，但是BOPP薄膜的断裂伸长率低于PVA薄膜；BOPP胶带、PVA热熔胶带、PVA水性胶带的拉伸强度分别为48.38，63.68，32.94 N/cm，BOPP胶带的断裂伸长率同时低于PVA热熔胶带和PVA水性胶带；BOPP胶带的初粘性略高于PVA水性胶带；BOPP胶带、PVA热熔胶带、PVA水性胶带的180°剥离强度分别为1.58，6.48，2.63 N/cm。结论 与BOPP胶带相比，PVA胶带的拉伸强度、断裂伸长率、初粘性和180°剥离强度均可满足封箱胶带对力学性能的要求。 |
| 英文摘要: |
| The work aims to substitute the non-degradable BOPP film with water-soluble PVA film as a tape substrate. Tensile strength and elongation at break of PVA film and BOPP film were respectively tested. Tensile strength, elongation at break, initial stickiness and 180° peel strength of PVA and BOPP films applied with water-based pressure sensitive adhesive and of PVA film applied with hot-melt adhesive were tested. The tensile strength of BOPP film was 34.32 N/cm, slightly higher than that of PVA film, but the elongation at break of BOPP film was lower than that of PVA film. The tensile strengths of BOPP tape, PVA hot-melt tape and PVA water-based tape were 48.38, 63.68 and 32.94 N/cm, respectively. The elongation at break of BOPP tape was lower than that of PVA hot-melt and water-based tapes. The initial stickiness of BOPP tape was slightly higher than that of PVA water-based tape. The 180° peel strength of BOPP tape, PVA hot-melt tape and PVA water-based tape were 1.58, 6.48 and 2.63 N/cm, respectively. Compared with BOPP tape, the tensile strength, elongation at break, initial stickiness and 180° peel strength of PVA tape can meet the requirement for mechanical properties of packaging tape. |
|